The growth of homoepitaxial GaN, AlGaN layers, and GaN/AlGaN multiple quantum wells (MQWs) on Ga- and N-faces of bulk GaN single crystal substrates prepared by pressure-controlled solution growth (PC-SG) has been performed by radio-frequency molecular-beam epitaxy (RF-MBE). It was determined that homoepitaxial GaN layers grown on both Ga- and N-faces had good crystallinity with narrow full-width at half maximum (FWHM) of 150 and 94 arcsec for the (0002) plane and 119 and 106 arcsec for the (10-12) plane in x-ray rocking curve measurements, respectively. Crack-free AlGaN epilayers with Al mole fraction up to 30% were obtained on both faces. AlGaN epilayers on Ga-faces with higher Al mole fraction than those on N-faces under the same Al flux condition were obtained. Furthermore, phase separation existed only in the AlGaN epilayers grown on N-faces. The 5 K photoluminescence spectra for the GaN/AlGaN MQW structures grown on Ga-faces at peak energy of 3.419 to 3.686 eV can be obtained by varying the well thickness from 18 to 2 ML.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.