This paper reports on SiGeSn/GeSn multi-quantum-well microdisk lasers. The fabrication of the devices includes a selective under-etching step, which enhances the guiding of the whispering gallery modes inside the cavity. Lasing occurs under different electrical pumping conditions with a very low threshold current and for long, quasi-continuous wave pulses compared to previously reported GeSn-based microdisk lasers. Furthermore, the lasing threshold current is reduced by a factor of ten compared to similar double-heterostructure devices.
We demonstrate Ge-on-Si avalanche photodiodes based on a separate absorption, charge, and multiplication structure using a novel double mesa structure. This double mesa structure effectively confines the electric field inside the diode, as confirmed through simulation data. This leads to a reduced contribution of charge carriers from interface states at the etched sidewalls to the dark current. The diodes exhibit a dark current reduction by a factor of 7 compared to a standard single mesa structure, while the optical properties remain unchanged. At a wavelength of 1310 nm, a maximum optical responsivity of 10.1 A/W, corresponding to a gain of 46, is achieved. Temperature-dependent dark current measurements showed an increase of the underlying activation energy from 0.13 eV to 0.28 eV. This results to a dark current of 0.14 nA at a temperature of 170 K and a bias voltage of 95 % VBD, which is approximately 100 times smaller than that of the single mesa APDs at 12.7 nA.
We demonstrate an in situ, non-invasive measurement method to ensure stable manufacturing and quality control of integrated waveguides. This method assumes that the scattered light from a waveguide is proportional to the propagating light inside the waveguide. Consequently, we can estimate the waveguide losses by measuring the scattered light along the waveguide. We compare this newly demonstrated measurement method with state-of-the-art methods, including Fabry-Perot interferometry, Mach-Zehnder Interferometry, ring resonator interferometry, and the cut-back method. To validate our measurement method’s working principle, we fabricated multiple amorphous silicon waveguides and characterized them using both, the presented and the cut-back method. Both methods yielded comparable results, indicating losses of around 1 dB/cm. For further investigation, multiple measurements of the same sample were conducted, resulting in a standard deviation of 0.29 dB/cm to 0.60 dB/cm. These initial standard deviations are sufficient to verify the presented measurement method. However, we want to emphasize that the main source of these deviations is due to the used measurement setup, indicating that the method has potential for improvement. Nevertheless, we have demonstrated that an in situ, non-invasive measurement of integrated waveguide losses is possible.
We present a suspended SiGeSn microring laser design that enables strain relaxation of the material layer stack, electrical pumping and adequate heat sinking. Using both strain and composition as two degrees of freedom to engineer the band structure, a direct bandgap is obtained in the gain material of a double heterostructure layer stack, and the L- to Γ-valley energy difference increased to 78 meV, by 66% compared to a non-underetched structure. The temperature dependent current threshold is modeled for the designed device and determined to be 18 kA/cm2 at 50 K. The fabrication process is outlined and first experimental electroluminescence results indicating the effectiveness of our approach are reported. At the time this proceedings paper is being submitted, electrically pumped lasing has also been achieved with a similar structure, with results that will be reported in a future publication.
In this paper, an ultra-thin buffer technology for the epitaxial growth of SixGe1-x-ySny structures on Si or Si-on-Insulator substrates by using molecular beam epitaxy is presented. This technology builds the basis for integrated photonic devices as detectors, modulators and light sources. The paper discusses different device families with different material compositions, which all use a relaxed Ge virtual substrate with high quality. These are pseudomorphic Ge/Ge1-ySny structures, SixGe1-x-ySny structures lattice matched to Ge and (partially) relaxed Ge1-ySny virtual substrates. The photonic devices consist of heterojunction diodes with vertical pin doping structures. As an example, Ge/Ge1-ySny multi quantum well photodetectors which active regions made from Nx(Ge0.93Sn0.07/Ge) multi-quantum well structures are presented. Optical measurements at high frequencies are successfully performed on these photodetectors. A 3-dB bandwidth above 40 GHz is measured at the optical telecommunication wavelength of 1550 nm.
To enlarge the tensile strain in Ge light emission diodes (s-Ge LED) we applied a GeSn virtual substrate (VS) on Si (001) with a Sn content of 4.5 %, to produce s-Ge LEDs. The LED stack was grown by molecular beam epitaxy. Electroluminescence investigations of the s-Ge LED show a major direct Ge peak and a minor peak at lower energy, which is formed by the GeSn-VS and the s-Ge indirect transition. The main peak of a 100 nm thick s-Ge LED is red-shifted as compared to the Ge peak of an unstrained reference Ge LED grown on Ge-VS. At a temperature of T = 80 K the increased tensile strain, produced by the GeSn-VS, causes a redshift of the direct Ge peak from 0.809 eV to 0.745 and 0.769 eV, namely for the s-Ge LED with a 100 and 200 nm thick active layer. At T = 300 K the direct Ge peak is shifted from 0.777 eV of the reference Ge LED to 0.725 eV (for 100 nm) and 0.743 eV (for 200 nm). The peak positions do not differ much between the 50 and 100 nm thick s-Ge LEDs. The intensities of the direct Ge peak increase with the s-Ge layer thickness. Moreover, the intensity of the 50 nm thick s-Ge sample is found to be larger than that of the 100 nm thick reference Ge LED.
Nanohole array surface plasmon resonance (SPR) sensors offer a promising platform for high-throughput label-free biosensing. Integrating nanohole arrays with group-IV semiconductor photodetectors could enable low-cost and disposable biosensors compatible to Si-based complementary metal oxide semiconductor (CMOS) technology that can be combined with integrated circuitry for continuous monitoring of biosamples and fast sensor data processing. Such an integrated biosensor could be realized by structuring a nanohole array in the contact metal layer of a photodetector. We used Fouriertransform infrared spectroscopy to investigate nanohole arrays in a 100 nm Al film deposited on top of a vertical Si-Ge photodiode structure grown by molecular beam epitaxy (MBE). We find that the presence of a protein bilayer, constitute of protein AG and Immunoglobulin G (IgG), leads to a wavelength-dependent absorptance enhancement of ~ 8 %.
The aim of integrating plasmonic functionality with photonic devices is twofold: on the one hand, plasmonic
nanoantennas can enhance the functionality of photonic devices and enable their miniaturization. On the other hand,
photonic devices can be a part of plasmonic transmission lines and act e.g. as plasmon detectors. Here, we present results
on both aspects in a CMOS-compatible device setup using Ge PIN-photodetectors and Al nanostructures. Plasmonic
nanoantennas are metallic nanostructures that enable the control and manipulation of optical energy in the visible and
near-infrared spectrum and have been proposed as a means to enhance absorption and quantum yields for photovoltaics,
to increase spatial resolution for optical microscopes and to enhance the energy efficiency of light-emitting devices. We
present experimental results on the enhancement of Ge PIN-photodetector efficiency by Al nanoantennas. In order to
investigate plasmon waveguiding and detection, metal grating structures and metal-insulator-metal slot waveguides were
fabricated by electron beam lithography in the Al metallization layer of Ge PIN-photodetectors. Photocurrent maps of
the devices under local illumination show that plasmons can be optically excited at the grating and are then guided by the
slot waveguide towards the Ge PIN-photodetector where they are detected as photocurrent. Using Ge PIN-photodetectors
and Al nanostructures as a CMOS-compatible device setup, we show how plasmonic nanostructures can be used for
efficiency enhancement of photonic devices and discuss plasmon detection with Ge PIN-photodetectors with possible
applications.
We analyzed Ge- and GeSn/Ge multiple quantum well (MQW) light emitting diodes (LEDs). The structures were grown
by molecular beam epitaxy (MBE) on Si. In the Ge LEDs the active layer was 300 nm thick. Sb doping was ranging
from 1×1018 to 1×1020 cm-3. An unintentionally doped Ge-layer served as reference. The LEDs with the MQWs consist
of ten alternating GeSn/Ge-layers. The Ge-layers were 10 nm thick and the GeSn-layers were grown with 6 % Sn and
thicknesses between 6 and 12 nm. The top contact of all LEDs was identical. Accordingly, the light extraction is
comparable.
The electroluminescence (EL) analysis was performed under forward bias at different currents. Sample temperatures
between <300 K and 80 K were studied. For the reference LED the direct transition at 0.8 eV dominates. With increasing
current the peak is slightly redshifted due to Joule heating. Sb doping of the active Ge-layer affects the intensity and at
3×1019 cm-3 the strongest emission appears. It is ~4 times higher as compared to the reference. Moreover a redshift of the
peak position is caused by bandgap narrowing.
The LEDs with undoped GeSn/Ge-MQWs as active layer show a very broad luminescence band with a peak around
0.65 eV, pointing to a dominance of the GeSn-layers. The light emission intensity is at least 17 times stronger as
compared to the reference Ge-LED. Due to incorporation of Sn in the MQWs the active layer should approach to a direct
semiconductor. In indirect Si and Ge we observed an increase of intensity with increasing temperature, whereas the
intensity of GeSn/Ge-MQWs was much less affected. But a deconvolution of the spectra revealed that the energy of
indirect transition in the wells is still below the one of the direct transition.
This work concentrates on the device characteristics and performance of Ge-on-Si p-i-n diodes for the use as absorption modulators. At first, the impact of temperature on electrical and on optical characteristics of these p-i-n diodes is investigated. Secondly, the feasibility of optical modulation using the Franz-Keldysh effect is demonstrated for temperatures up to 359 K. The Ge-on-Si p-i-n diodes are grown using a molecular beam epitaxy system. The layer structure includes a double Si/Ge-heterojunction and an intrinsic zone with a thickness of 500 nm. During the growth process several annealing steps are performed to reduce the dislocation density and incorporate tensile strain in the intrinsic zone. The dark current is proportional to the diode area and amounts to 40 mA/cm2 at a reverse voltage of 1 V. An analysis of the temperature dependence of the dark current shows that it is dominated by generation/recombination of carriers probably at threading dislocations. The optical absorption spectra recorded show a shrinkage of the infrared cut off wavelength of about 0.6 nm/K. In addition the change of absorption at the direct bandedge with different applied biases, i.e. the Franz- Keldysh effect, is demonstrated for temperatures from 300 K to 359 K. With regard to modulation of an optical signal the on/off ratio is evaluated as function of the voltage swing. With a moderate voltage swing of 2 V the maximal absorption change is 300 cm-1 and the optimal working regime shifts from 1625 nm at 300 K to 1665 nm at 337 K.
This work presents the limiting factors of fast Germanium p-i-n photodetectors for optical on-chip communication. The photodetectors are grown by molecular beam epitaxy on Silicon and Silicon on insulator substrates. On-wafer RF and optical RF measurements up to 40 GHz are performed at a wavelength of 1.55 μm. Different de-embedding procedures are used to obtain the amplitude and phase of the device impedance and the equivalent circuit description. An analysis of the reflection coefficient compared to the equivalent circuit explains the frequency characteristic and it is used to determine background doping of the intrinsic layer and the expansion of the space charge width. The optical bandwidth is measured for different bias voltages and background doping. The RC limitation of the detectors is shown and analyzed leading to adjusted parameters for high speed detectors at zero-bas.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.