Phase degradation characteristics of programmed AAPSM defects with automatic inspection tool sensitivity

Darren Taylor; Eric Poortinga

doi:10.1117/12.518065

17 December 2003 Phase degradation characteristics of programmed AAPSM defects with automatic inspection tool sensitivity

Darren Taylor, Eric Poortinga

Author Affiliations +

Proceedings Volume 5256, 23rd Annual BACUS Symposium on Photomask Technology; (2003) https://doi.org/10.1117/12.518065
Event: Photomask Technology, 2003, Monterey, California, United States

Abstract

Accurate defect characterization is becoming increasingly more important with the increased implementation of AAPSM applications. Quartz bump/divot defectivity adds a third dimension to the historical definition of photomask defects that included only size and transmission. This new dimension is phase. Past studies have suggested that significant phase degradation occurs even at smaller defect sizes. This characterization is tied closely with the defect capture capability of photomask inspection. Inspection tool sensitivity to phase defects is increasingly important for at least two reasons: the danger of catastrophic defects printing on the wafer, and the newness of these types of defects to the photomask-making community at large. This experiment utilizes two distinct forms of defect characterization -- SEM sizing and surface profilometry. Programmed defect test masks were manufactured for phase shifting properties at both 248nm and 193nm exposure wavelengths. The defects were etched at multiple depths resulting in a variety of phase angle errors. This study will examine the effects of phase degradation on smaller defects along with defect capture from automatic inspection tools.

Citation Download Citation

Darren Taylor and Eric Poortinga "Phase degradation characteristics of programmed AAPSM defects with automatic inspection tool sensitivity", Proc. SPIE 5256, 23rd Annual BACUS Symposium on Photomask Technology, (17 December 2003); https://doi.org/10.1117/12.518065

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available